2205 chalybs immaculata 4*1mm capillares amplexus tubinge
2205 Duplex Steel plexus capillaris tubing
Mechanica Duplex Steel Grade 2205
2205 chalybs immaculata 4*1mm capillares amplexus tubinge
| Gradus | Str distrahens (MPa) min | Cedat imperium 0.2% Probatur (MPa) min | Prolongatio (% in 50mm) min | Duritia-Rockwell C (HR C) | Duritia Brinell (HB) |
|---|---|---|---|---|---|
| 2205 | 621 | 448 | 25 | 31 max | 293 max |
Corporalia Duplex Steel 2205
2205 chalybs immaculata 4*1mm capillares amplexus tubinge
| Densitas (Kg.m-1) | 7810 |
|---|---|
| Magnetic Permeability | <50 |
| Modulus (N/mm2) | 190* 10^3 |
| Imprimis Caloris, 20°℃(J.Kg-1.°K-1) | 400 |
| Imprimis Resistentia Electrical, 20℃(uO.m) | 0.85 |
| Scelerisque conductivity,20℃ | 15 |
| Medium coefficiens scelerisque expansion | 11*10^6 |
2205 Duplex Steel Chemical Composition:
2205 chalybs immaculata 4*1mm capillares amplexus tubinge
| Grades | C | Mn | Si | P | S | Cr | Mo | Ni | N |
|---|---|---|---|---|---|---|---|---|---|
| 2205 (S31803) | ≤0.03 | ≤2.0 | ≤1.0 | ≤0.03 | ≤0.02 | 21.0≤Cr≤23.0 | 2.5≤Mo≤3.5 | 4.5≤Ni≤6.5 | 0.08≤N≤0.20 |
| 2205 (S32205) | ≤0.03 | ≤2.0 | ≤1.0 | ≤0.03 | ≤0.02 | 21.0≤Cr≤23.0 | 3.0≤Mo≤3.5 | 4.5≤Ni≤6.5 | 0.14≤N≤0.20 |
2205 chalybs immaculata 4*1mm capillares amplexus tubinge
Signa Duplex Ss 2205;
- ASTM/ASME: A240 UNS S3220/S31803
- EURONORM: 1.4462 X2CrNiMoN 22.5.3
- AFNOR: Z3 CrNi 22.05 AZ
- DIN: W.Nr 1.4462
Applications Duplex Ss 2205
2205 chalybs immaculata 4*1mm capillares amplexus tubinge
Aliquae applicationes typicae gradus chalybis immaculati duplex 2205 infra recensentur:
- Oleum et gas exploratio
- Processus armorum
- Vehicula, repono, et chemicae processus
- Princeps chloride et marinus ambitus
- Chartae machinae, piscinae liquoris, pulpae, chartae digestores, etc.
Features Duplex Ss 2205
2205 chalybs immaculata 4*1mm capillares amplexus tubinge
Duplex Steel immaculatus 2205 Comparatus cum 316L et 317L austeniticis chalybus immaculatis, 2205 superior est in resistentia anti pituitae et rimae corrosionis.Princeps corrosionis resistentia habet.Comparatus cum austenite, dilatatio scelerisque coefficientis est inferior, scelerisque conductivity superior est.
Duplex Steel Immaculatus 2205 bis vim compressivam habet ferri austenitici immaculati, permittens designatores ad pondus reducendum comparatum 316L et 317L.2205 mixtura aptissima est usui in -50° F/ + 600° F range temperatura et adhiberi potest ad temperaturas inferiores sub gravibus restrictionibus (praesertim pro constructione iuncta).
Corrosio resistentiae 2205 Duplex Steel
2205 chalybs immaculata 4*1mm capillares amplexus tubinge
- Corrosio uniformis, Corrosio resistentia duarum ferro immaculatorum 2205 praestantior est 316L et 317L in plerisque ambitus propter chromium contentum (22%), molybdenum (3%), et nitrogenium (0,18%).
Locus anti-corrosionis, Contentum chromii, molybdaeni et nitrogenii in ferro inauto duplo 2205 reddit, valde repugnant in solutionibus oxydizationis et acidicae pituitae et rimae corrosioni. - Anti- vis corrosio, 2205 Duplex structura ferri incorrupti adiuvat ad meliorem resistentiam ad accentus corrosionem rimas ferro immaculati.In quadam temperatura, sub conditionibus tensionis, oxygenii, et chloridi, accentus corrosio chloride in austenitico ferro immaculato occurrit.Cum hae condiciones non facile moderantur, usus 304L, 316L et 317L hac in re limitantur.
- Anti-corrosio lassitudo, Dual-phase ferrum 2205 altum robur et corrosio resistentia ad corrosionem altum resistendi lassitudine virium.Armorum processus susceptibilis ad ambitus exesos et cyclos onerandos, et duplex ferrum immaculatum 2205 lineamenta talium applicationum bene apta sunt.
Metallographia de Duplex Ss 2205 uns s31803
Compositio chemica ferri 2205 dupplex microstructuram desideratam 50 / 50 post 1900 / 1922° F (1040 °C / 1080°C) solidam furnum solutionem dat.Si calor curatio temperatura MM° F altior est, potest ducere ad compositionem ferrite augendam.Sicut aliae ferrum immaculatum duplex, 2205 mixturae susceptibiles sunt ad intermetallicis phases praecipitatio.
Phase intermetallica inter 1300° F et 1800° F praecipitat ac velocissime praecipitat in 1600° F. Ergo opus est probare 2205, ut nulla intermetallica periodus, test referat ASTM A 923 .