Gradus 310 medium carbonis austeniticum est ferrum immaculatum, nam applicationes caliditas sicut partes fornacis et instrumenti curationis caloris.Temperaturis usque ad 1150°C adhibetur in continua servitio, et 1035°C in servitio intermisso.Gradus 310S est humilis versio carbonis gradus 310 .
Applications Grade 310/310S Steel
310S immaculatam ferro plexu Tubing
Applicationes typicae Gradus 310/310S adhibentur in strato fluido combustores, fornacibus, tubis radiantibus, tubus adseculae ad petrolei expolitionem et ferventem bullientem, gasificantem carbonum partium internarum, ollas plumbeas, thermowellas, ancoras refractarias, turibula et cryptas combustiones, retorsiones, mufculos; furnum opercula, saggers, cibum processus armorum, structuras cryogenicas.
Proprietates Grade 310/310S Steel
310S immaculatam ferro plexu Tubing
Hi gradus 25% chromium et 20% nickel continent, eosque oxidationis et corrosioni valde repugnant.Gradus 310S versio carbonis inferior est, minor proclivior ad aebrietatem et sensibilitatem in servitio.Chromium altum et medium nickel contentum faciunt hos chalybes aptas ad applicationes ad atmosphaeras sulphuris reducendas in quibus H2S.Late adhibentur in atmosphaerae carburising mediocriter, sicut in ambitu petrochemico offendit.Ad atmosphaeras carburising graviores aliae caloris admixtiones resistentes eligendae sunt.Gradus 310 non commendatur crebris humoribus exstinguiendis sicut infertur a scelerisque incursu.Gradus saepe adhibetur in applicationibus cryogenicis, propter duritiem et permeabilitatem magneticam humilem.
Commune cum aliis austeniticis ferro immaculatis, hi gradus per curationem caloris indurari non possunt.Frigore laborare possunt, sed hoc raro exercetur.
Chemcial Compositio Grade 310/310S Steel
310S immaculatam ferro plexu Tubing
Compositio chemica gradus 310 et gradus 310S chalybis immaculati in sequenti tabula perstringuntur.
Mensam 1 .Compositio chemica gradus 310 et 310S% chalybs immaculata
310S immaculatam ferro plexu Tubing
| Compositio chemica | 310 | 310S |
| Carbon | 0.25 max | 0.08 max |
| Manganese | 2.00 max | 2.00 max |
| Pii | 1.50 max | 1.50 max |
| Phosphorus | 0.041 max | 0.041 max |
| Sulphur | 0.030 max | 0.030 max |
| Chromium | 24.00 – 26.00 | 24.00 – 26.00 |
| Nickel | 19.00 – 22.00 | 19.00 – 22.00 |
Mechanica Grade 310/310S Steel
Mechanica proprietas gradus 310 et gradus 310S chalybe immaculati perstringuntur in sequenti tabula.
Tabula II.Mechanica gradus 310/310S immaculatam ferro
| Mechanica Properties | 310/ 310S |
| Gradus 0.2% Probatur vis MPa (min) | 205 |
| Distrahens fortitudo MPa (min) | 520 |
| Prolongatio % (min) | 40 |
| Duritia (HV) (max) | 225 |
Corporalia proprietates Ferritic Steel
Corporales proprietates gradus 310 et gradus 310S ferro immaculati perstringuntur in sequenti tabula.
Tabula III.Corporalia gradus 310/310S immaculatam ferro
| Properties | at | Precium | Unitas |
| Density |
| 8,000 | Kg/m3 |
| Electrical Conductivity | 25°C | 1.25 | %IACS |
| Resistivity electrica | 25°C | 0.78 | Micro ohm.m |
| Modulus Elasticitatis | 20°C | 200 | GPa |
| tondendas Modulus | 20°C | 77 | GPa |
| Poisson's Ratio | 20°C | 0.30 |
|
| Exustio Rnage |
| 1400-1450 | °C |
| Imprimis Caloris |
| 500 | J/kg.°C |
| Relativum Magnetic Permeability |
| 1.02 |
|
| Scelerisque conductivity | 100°C | 14.2 | W/m.°C |
| Coefficiens Expansion | 0-100°C | 15.9 | /°C |
| 0-315°C | 16.2 | /°C | |
| 0-540°C | 17.0 | /°C |
Post tempus: Iun-07-2023