| Standard | Steel Gradus | ||||||||
|---|---|---|---|---|---|---|---|---|---|
| Chemical compositione % | |||||||||
| C: | Mn: | Si: | P: | S: | Cr: | Ni: | Mo: | N: | |
| EN | 1.4401 - X5CrNiMo17-12-2 | ||||||||
| <0.07 | <2.0 | <1.0 | <0.045 | <0.015 | 16.5 – 18.5 | 10.0 – 13.0 | 2.0 – 2.5 | <0.11 | |
| EN | 1.4404 - X2CrNiMo17-12-2 | ||||||||
| <0.03 | <2.0 | <1.0 | <0.045 | <0.030 | 16.5 – 18.5 | 10.0 – 13.0 | 2.0 – 2.5 | <0.11 | |
| ASTM | AISI 316 - TP316 - UNS S31600 | ||||||||
| <0.08 | <2.0 | <1.0 | <0.045 | <0.030 | 16.0 – 18.0 | 10.0 – 14.0 | 2.0 - 3.0 | - | |
| ASTM | AISI 316L - TP316L - UNS S31603 | ||||||||
| <0.08 | <2.0 | <0.8 | <0.045 | <0.030 | 16.0 – 18.0 | 11.0 – 14.0 | 2.0 – 2.5 | - | |
| PN | 00H17N14M2 | ||||||||
| <0.03 | <2.0 | <0.8 | <0.045 | <0.030 | 16.0 – 18.0 | 12.0 – 15.0 | 2.0 – 2.5 | - | |
| GOST | 03Ch17N13M2 - 03Х17Н13М2 | ||||||||
| <0.03 | 1.0 – 2.0 | <0.4 | <0.030 | <0.020 | 16.8 – 18.3 | 13.5 – 15.0 | 2.2 – 2.8 | - | |
| NF | Z3CND17-11-02 | ||||||||
| <0.03 | <2.0 | <1.0 | <0.040 | <0.030 | 16.0 – 18.0 | 10.0 – 12.0 | 2.0 – 2.5 | - | |
| NF | Z7CND17-11-02 | ||||||||
| <0.07 | <2.0 | <1.0 | <0.040 | <0.030 | 16.0 – 18.0 | 10.0 – 12.0 | 2.0 – 2.5 | - | |
1.4404, 1.4401, AISI 316/L
Austeniticum chalybe immaculatum repugnat corrosioni intergranulari, maxime adhibito in ambitibus chloridis noxiis, acida et urea continentibus.316/316L gradus est fundamentalis e globo CrNiMo cum Molybdeno, cuius adiectio insigniter auget resistentiam ad corrosionem ferri per 2-3 vicibus fovendi et rimas.
Materiae in gradu 1.4404/1.4401 usui aptae sunt in ambitu phosphorici, nitrici, citrici, lactici, formici, acetici, coram alcali - hydroxide, salibus - nitrates, chlorides, fluorides, acetates et sulphates.Gradus etiam resistentiam ostendit ambitui marino et salibus.Ferrum non repugnat acido chlorico, acido orthophosphorico, acidi formic in concentratione alto, acido sulphurico et acido hydrochlorico.
316L chalybis immaculatis 4*0.5mm capillaribus tubingis
316 et 316L producta propria sunt per resistentiam ad caliditates, altam plasticitatem, ductilis, et relative bona ductilis.Aptissima sunt compressionis, frigoris et distrahentiae obdurationes ad fontes producendos et fontium elementa ex fasciolis vel filis.Materiae proprietates non magneticae in molli conditione ostendunt, bonas proprietates mechanicas in temperaturae cryogenicas et bonae weldability non requirunt additional processuum curationi caloris.Gravis etiam est notare proprietates mechanicas respective humiles, quae non conducunt ad applicationes mechanicas et difficile machinabilitatem ferri.
316L chalybis immaculatis 4*0.5mm capillaribus tubingis
Ferro 316/L nec non 1.4404/1.4401 late usus est in oleo, nitrogen, fabricando, chemico, constructione, conflatorio, medicinali, celluloso, cryogenico, automotivo, nec non in esculentis processus industriis in modum laminarum, taperum, tibiarum. manicas, caerimonias, malleolos, vectes, partes officinarum gasi, nummariorum caloris, cancelli, apparatum navis et vehicula oneraria publica, valvulae, lacus, soleatus, radiatores, machinis cibi processus in lacticiniis, obsonationibus, carnibus plantarum, vegetabilium et fructuum processus. plantae, distillatores, caminis, systemata vaporaria, pipelinea, instrumentum pressus, crystallizatores, cisternae, silos, lacus natantes, partes boiles, condensatores, autoclaves, reactoria vel instrumentum densationis.
316L chalybis immaculatis 4*0.5mm capillaribus tubingis
Post tempus: Iun-20-2023