Chalybes immaculati sunt altae admixtionis, quae alte corrosionem habent resistentiam quam alii ferrei propter praesentiam magni ponderis chromii in 4 ad 30% percursum.Ferri immaculati in martensiticis, ferriticis et austeniticis in structura cristallina eorum collocantur.Additoton, aliam globi speciem formant quae ferros praecipitatio-duratos, quae sunt ex ferro martensitico et austenitico compositum.
347H intemerata tortum ferro Tubing
Sequentia schedula accuratius providebit de gradu 347H intemerato ferro, quod paulo durior est quam gradus 304 ferri.
347H intemerata tortum ferro Tubing
Sequens tabula ostendit compositionem chemicam gradus 347H ferro immaculatam.
347H intemerata tortum ferro Tubing
| Elementum | Content (%) |
|---|---|
| Ferrum, Fe | 62.83 – 73.64 |
| Chromium, Cr | 17 – 20 |
| Nickel, Ni | 9 – 13 |
| Manganum | 2 |
| Pii, Si | 1 |
| Niobium, Nb (Columbium, Cb) ; | 0.320 - 1 |
| Carbon, C | 0.04 - 0.10 |
| Phosphorus, P | 0.041 |
| Sulphur, S | 0.030 |
Corporalia Properties
347H intemerata tortum ferro Tubing
Proprietates physicae gradus 347H chalybe immaculato traduntur in sequenti tabula.
| Properties | Metric | Imperiale |
|---|---|---|
| Density | 7.7 – 8.03 g/cm3 | 0.278 – 0.290 lb/in³ |
347H intemerata tortum ferro Tubing
Mechanica Properties
Mechanica proprietas gradus 347H ferrum immaculatum in sequenti tabula exhibetur.
| Properties | Metric | Imperiale |
|---|---|---|
| Robur distrahens, ultimate | 480 MPa | 69600 psi |
| Distrahentes vires, cede | 205 MPa | 29700 psi |
| Robur rupta (@ 750° C/1380°F, hora 100,000 horarum) | 38 – MPa, 39 | 5510 – 5660 psi |
| Modulus elasticus | 190 – 210 GPa | 27557 – 30458 ksi |
| Ratio Poisson | 0.27 - 0.30 | 0.27 - 0.30 |
| Prolongatio ad intermissum | 29% | 29% |
| Duritia, Brinell | 187 | 187 |
Aliae notiones quae gradu 347H immaculatae ferro aequiparantur sequentes includuntur:
- ASTM A182
- ASTM A213
- ASTM A240
- ASTM A249
- ASTM A271
- ASTM A312
- ASTM A336
- ASTM A376
- ASTM A403
- ASTM A430
- ASTM A479
- ASTM A813
- ASTM A814
- SAE 30347H