Gradus 310/310S chalybs immaculatus 8.0*0.3mm amplexus tubing/capillares tubing
Chemcial Compositio Grade 310/310S Steel
Compositio chemica gradus 310 et gradus 310S chalybis immaculati in sequenti tabula perstringuntur.
Gradus 310/310S chalybs immaculatus 8.0*0.3mm amplexus tubing/capillares tubing
Mensam 1 .Compositio chemica gradus 310 et 310S% chalybs immaculata
| Compositio chemica | 310 | 310S |
| Carbon | 0.25 max | 0.08 max |
| Manganese | 2.00 max | 2.00 max |
| Pii | 1.50 max | 1.50 max |
| Phosphorus | 0.041 max | 0.041 max |
| Sulphur | 0.003 max | 0.003 max |
| Chromium | 24.00 – 26.00 | 24.00 – 26.00 |
| Nickel | 19.00 – 22.00 | 19.00 – 22.00 |
Mechanica Grade 310/310S Steel
Mechanica proprietas gradus 310 et gradus 310S chalybe immaculati perstringuntur in sequenti tabula.
Gradus 310/310S chalybs immaculatus 8.0*0.3mm amplexus tubing/capillares tubing
Tabula II.Mechanica gradus 310/310S immaculatam ferro
| Mechanica Properties | 310/ 310S |
| Gradus 0.2% Probatur vis MPa (min) | 205 |
| Distrahens fortitudo MPa (min) | 520 |
| Prolongatio % (min) | 40 |
| Duritia (HV) (max) | 225 |
Corporalia proprietates Ferritic Steel
Corporales proprietates gradus 310 et gradus 310S ferro immaculati perstringuntur in sequenti tabula.
Gradus 310/310S chalybs immaculatus 8.0*0.3mm amplexus tubing/capillares tubing
Tabula III.Corporalia gradus 310/310S immaculatam ferro
| Properties | at | Precium | Unitas |
| Density |
| 8,000 | Kg/m3 |
| Electrical Conductivity | 25°C | 1.25 | %IACS |
| Resistivity electrica | 25°C | 0.78 | Micro ohm.m |
| Modulus Elasticitatis | 20°C | 200 | GPa |
| tondendas Modulus | 20°C | 77 | GPa |
| Poisson's Ratio | 20°C | 0.30 |
|
| Exustio Rnage |
| 1400-1450 | °C |
| Imprimis Caloris |
| 500 | J/kg.°C |
| Relativum Magnetic Permeability |
| 1.02 |
|
| Scelerisque conductivity | 100°C | 14.2 | W/m.°C |
| Coefficiens Expansion | 0-100°C | 15.9 | /°C |
| 0-315°C | 16.2 | /°C | |
| 0-540°C | 17.0 | /°C |