General Properties
Admisce 2205 duplex lamina ferro immaculata est 22% Chromium, 3% Molybdenum, 5-6% Nickel NITROGENIUM mixtum duplex laminam immaculatam ferro cum magno generali, locali et accentus corrosionis resistentiae proprietates praeter altitudinem roboris et excellentem ictum duritiem.
2205 ferro intemerata amplexu tubinge
Admisce 2205 duplex lamina ferro immaculata fovere et rimas corrosioni resistentiae praebet superior 316L vel 317L ferrum austeniticum immaculatum in omnibus fere instrumentis mordax.Etiam altum corrosio et exesa lassitudine proprietatum tum minorum expansionum scelerisque ac superiorum scelerisque conductivity quam austeniticae.
Vires cedere de bis est ferreis austeniticis immaculatis.Hoc permittit excogitatoris ad pondus servandum et stannum magis competitive pretium efficit comparatum ad 316L vel 317L.
2205 ferro intemerata amplexu tubinge
Admisce 2205 duplex lamina ferrea immaculata, aptissima est maxime apta applicationibus ad -50°F/+600°F range temperaturas.Temperaturae extra hunc ambitum considerari possunt, sed restrictionibus nonnullis indigent, praesertim ad structuras iunctas.
2205 ferro intemerata amplexu tubinge
Corrosio Resistentia
General Corrosio
Propter altitudinem suum chromium (22%), molybdenum (3%), et nitrogenium (0.18%) contentorum, corrosio resistentiae proprietatum 2205 laminae chalybis immaculatae duplicae potiores sunt quam 316L vel 317L in plerisque ambitibus.
Localised Corrosio Resistentia
Chromium, molybdenum et nitrogenium 2205 duplex lamina ferro immaculata, etiam repugnantiam praestantem praebent ad corrosionem fovendum et rima etiam in solutionibus valde oxidentibus et acidicis.
Isocorrosion curvarum 4 mpy (0.1 mm/yr), in solutione acidi sulphurici continens 2000 ppm
Suspendisse Corrosio Resistentia
Duplex microstructura nota est emendare vim corrosionis creptionis resistentiae chalybi immaculati.
Chloride accentus corrosio crepuit ferrorum austeniticorum immaculatorum fieri potest cum condiciones necessariae temperaturae, accentus distrahentes, oxygeni, et chlorides adsunt.Cum hae condiciones non facile contineantur, vis corrosio crepuit saepe impedimentum adhibitis 304L, 316L, 317L.
2205 ferro intemerata amplexu tubinge
Corrosio lassitudo resistentiae
2205 Duplex lamina immaculata Admiscuit ferro magno robore dissociatur, et alte corrosio resistit, ut corrosio lassitudine producat altum robur.Applicationes in quibus apparatu processui obnoxius est tum ambitus mordax, tum cycli onerationes ex proprietatibus bracteae 2205 dupli immaculatae ferri.
Critica Pitting Temperature in 1M NaCl Mensurata utens in Outokumpu Aliquam, Inc Pitting Cell
Critical Crevice Corrosio Temperature (CCT) in 10% FeCl3•6H2O
Corrosio generalis in Processu humido phosphoric acidis
| Corrosio Rate, ipy | ||||||||
|---|---|---|---|---|---|---|---|---|
| Gradus | Solutio A, 1401/4F | Solutio B, 1201/4F | ||||||
| 2205 | 3.1 | 3.9 | ||||||
| 316L | >200 | >200 | ||||||
| 904L | 47 | 6.3 | ||||||
| Compositio, wt% | ||||||||
| P2O5 | HCl | HF | H2SO4 | Fe2O3 | Al203 | SiO2 | CaO' | MgO |
| Sol A 54.0 | 0.06 | 1.1 | 4.1 | 0.27 | 0.17 | 0.10 | 0.20 | 0.70 |
| Sol B 27.5 | 0.34 | 1.3 | 1.72 | 0.4 | 0.001 | 0.3 | 0.02 | - |
Suspendisse Corrosio Cracking Repugnantia
| Fervens | Wick | Fervens | |
|---|---|---|---|
| Gradus | 42% MgCl2 | Test | 25% NaCl |
| 2205 | F | P | P |
| 254 SMO® | F | P | P |
| Typus 316L | F | F | F |
| Typus 317L | F | F | F |
| Admisce 904L | F | P vel F * | P vel F * |
| Admisce 20 | F | P | P |
(P = Pass, F = Fail)
Chemical Analysis
Typical Pretio (% pondus)
| Carbon | Chromium | Nickel | Molybdenum | Nitrogen | alii |
|---|---|---|---|---|---|
| 0.018 | 22.1 | 5.6 | 3.1 | 0.18 | S=0.001 |
| PREN = [Cr%] = 3.3 [Mo%] = 16 [N%] ≥ 34 | |||||
Mechanica Properties
Mechanica Properties apud volutpat Temperature
| ASTM A 240 | Typical | |
|---|---|---|
| Fortitudo 0.2% cede, ksi | 65 min. | 74 |
| Fortitudo distrahens, ksi | 90 min. | 105 |
| Prolongatio, % | 25 min. | 30 |
| duritia RC | max XXXII. | 19 |
Distrahentes Properties ad Elevatum Temperaturis
| Aequaliter Nubila °F | 122 | 212 | 392 | 572 |
|---|---|---|---|---|
| Fortitudo 0.2% cede, ksi | 60 | 52 | 45 | 41 |
| Fortitudo distrahens, ksi | 96 | 90 | 83 | 81 |
Corporalia Properties
| Aequaliter Nubila °F | 68 | 212 | 392 | 572 | |
|---|---|---|---|---|---|
| Density | lb/in3 | 0.278 | - | - | - |
| Modulus Elasticitatis | psi x 106 | 27.6 | 26.1 | 25.4 | 24.9 |
| Linearibus expansio (68°FT) | 10-6/°F | - | 7.5 | 7.8 | 8.1 |
| Scelerisque conductivity | Btu/h ft°F | 8.7 | 9.2 | 9.8 | 10.4 |
| Calor Capacitas | Btu/lb ft°F | 0.112 | 0.119 | 0.127 | 0.134 |
| Resistivity electrica | Ωin x 10-6 | 33.5 | 35.4 | 37.4 | 39.4 |