Introductio
Dives immaculatus nota est summus admixto ferro.Consistunt circiter 4-30% chromii.In chalybis martensiticis, austeniticis et ferriticis, in structura crystallina, collocantur.
Gradus 317 Immaculata chalybs est modificata versio 316 Immaculata ferro.Magna vis est et corrosio resistentia.Sequentia schedula plura de gradu 317 ferro immaculato dat.
Compositio chemica
Stainless Steel - Grade 317 (UNS S31700)
Compositio chemica gradus 317 chalybs immaculata in sequenti tabula delineatur.
| Elementum | Content (%) |
|---|---|
| Ferrum, Fe | 61 |
| Chromium, Cr | 19 |
| Nickel, Ni | 13 |
| Molybdenum, Mo | 3.50 |
| Manganum | 2 |
| Pii, Si | 1 |
| Carbon, C | 0.093 |
| Phosphorus, P | 0.041 |
| Sulphur, S | 0.030 |
Corporalia Properties
Stainless Steel - Grade 317 (UNS S31700)
Sequens tabula ostendit corporis proprietates gradus 317 ferro immaculatam.
| Properties | Metric | Imperiale |
|---|---|---|
| Density | 8 g/cm3 | 0.289 lb/in³ |
| Liquescens punctum | 1370°C | 2550°F |
Mechanica Properties
Stainless Steel - Grade 317 (UNS S31700)
Mechanica proprietas annatae gradus 317 chalybs immaculata in tabula sequenti monstratur.
| Properties | Metric | Imperiale |
|---|---|---|
| Distrahentes fortitudo | 620 MPa | 89900 psi |
| Cedat imperium | 275 MPa | 39000 psi |
| Modulus elasticus | 193 GPa | 27993 ksi |
| Ratio Poisson | 0.27-0.30 | 0.27-0.30 |
| Prolongatio in luce (in 50 mm) | 45% | 45% |
| Duritia, Rockwell B | 85 | 85 |
Scelerisque Properties
Thermae proprietates gradus 317 ferro immaculato dantur in tabula sequenti.
| Properties | Metric | Imperiale |
|---|---|---|
| Scelerisque dilatatio co-efficiens (@ 0-100° C/32-212°F) | 16 µm/m°C | 8.89 µin/in°F |
| Scelerisque conductivity (@ 100°C/212°F) | 16.3 W/mK | 113 BTU in/hr.ft².°F |
Aliae Vocabula
Aliae designationes aequivalentes gradu 317 ferro immaculato in tabula sequenti comprehenduntur.
| ASTM A167 | ASTM A276 | ASTM A478 | ASTM A814 | ASME SA403 |
| ASTM A182 | ASTM A312 | ASTM A511 | QQ S763 | ASME SA409 |
| ASTM A213 | ASTM A314 | ASTM A554 | DIN 1.4449 | MIL-S-862 |
| ASTM A240 | ASTM A403 | ASTM A580 | ASME SA240 | SAE 30317 |
| ASTM A249 | ASTM A409 | ASTM A632 | ASME SA249 | SAE J405 (30317) |
| ASTM A269 | ASTM A473 | ASTM A813 | ASME SA312 |
Fabricatio et calor curatio
Machinability
Quaeris apparatum ad resolvere metalla tua?
317 intemerata gracie durior est ferro, 304 ferro intemerata, .Commendatur ruptoribus uti chip.Hardenbilitas huius mixturae minuetur si assidue alit et infimae velocitates adhibeantur.
Welding
Gradus 317 ferrum immaculatum conflari potest utendi modos fusionis et resistentiae.Methodus oxyacetyleni glutini huic offensioni non praefertur.AWS E/ER317 vel 317L metalli filli adhiberi possunt ad bonum exitum consequendum.
Calidum Operationis
Gradus 317 ferrum immaculatum calidum exerceri potest utens omnes rationes operationes communes calidas.1149-1260°F calefactum est.Non calefieri infra 927°C (1700°F).Furnum post-opus fieri potest ut proprietas resistentiae corrosionis retineat.
Frigus Operationis
Pressio, tonsura, extractio, et petitio feliciter fieri potest.Furnum post-opus fit ut accentus internus minuatur.
Post tempus: Mar-09-2023